Clarnate® FL5073
| Property Name | Value | Unit |
|---|---|---|
| Appearance | Powder | -- |
| Physical State | Solid | -- |
| Relative density (water = 1) | 1.18-1.20 | -- |
| Auto-Ignition Temperature | >450 | °C |
| Decomposition Temperature | >380 | -- |
| Solubility in Water | Immiscible | -- |
| Specification Name | Value | Unit | Test Method | Test Condition |
|---|---|---|---|---|
| Melt Flow Index at 300°C/1.2 Kg | 7 | g/10min | ASTM D1238 | -- |
| Mold Shrinkage | 0.5 - 0.7 | % | ASTM D955 | -- |
| Water Absorption at 23°C, 24h | 0.2 | % | ASTM D570 | -- |
| Density | 1.2 | g/cm3 | ASTM D792 | -- |
| Stress at Break at 50 mm/min | 72 | MPa | ASTM D638 | -- |
| Tensile Modulus at 1 mm/min | 2300 | MPa | -- | -- |
| Yield Stress at 50 mm/min | 65 | MPa | -- | -- |
| Yield Strain at 50 mm/min | 6 | % | -- | -- |
| Strain at Break at 50 mm/min | 120 | % | -- | -- |
| Flexural Strength at 2 mm/min | 96 | MPa | ASTM D790 | -- |
| Flexural Modulus at 2 mm/min | -- | MPa | -- | -- |
| Izod Notched Impact Strength at 23 °C | 800 | J/m | ASTM D256 | -- |
| Heat Distortion Temp. at 1.82 MPa; 3.2 mm | 130 | °C | ASTM D648 | -- |
| Vicat Softening Temp. at 120 °C/h; 50 N | 151 | °C | ASTM D1525 | -- |
| Haze at 3 mm | < 0.8 | % | ASTM D1003 | -- |
| Light Transmittance at 3 mm | 89 | % | -- | -- |
| Refractive Index | 1.586 | -- | ASTM D542 | -- |
| Flame Rating at 3 mm | HB | -- | UL 94 | -- |
| Flame Rating at 1.5mm | V2 | -- | -- | -- |
| Relative Permittivity at 100 Hz | 3.1 | -- | IEC 60250 | -- |
| Relative Permittivity at 1 MHz | 3 | -- | -- | -- |
| Dissipation Factor at 100 Hz | 5 | 10^-4 | -- | -- |
| Dissipation Factor at 1 MHz | 90 | 10^-4 | -- | -- |
| Volume Resistivity | 10^14 | Ω·m | IEC 60093 | -- |
| Surface resistivity | 10^16 | Ω | -- | -- |
| Electric Strength at 1 mm | 34 | kV/mm | IEC 60243-1 | -- |
| Comparative Tracking Index at Solution A | 250 | V | IEC 60112 | -- |
| Drying Temperature | -- | °C | -- | -- |
| Drying Time | -- | h | -- | -- |
| Injection Temperature | 280 - 310 | °C | -- | -- |
| Mold temperature | 80 | °C | -- | -- |
| Injection Speed | 50 | mm/s | -- | -- |
| Specification Name | Value | Unit | Test Method | Test Condition |
|---|---|---|---|---|
| Melt Flow Index at 300°C/1.2 Kg | 10 | g/10min | ASTM D1238 | -- |
| Mold Shrinkage | 0.5 - 0.7 | % | ASTM D955 | -- |
| Water Absorption at 23°C, 24h | 0.2 | % | ASTM D570 | -- |
| Density | 1.2 | g/cm3 | ASTM D792 | -- |
| Stress at Break at 50 mm/min | 72 | MPa | ASTM D638 | -- |
| Tensile Modulus at 1 mm/min | 2300 | MPa | -- | -- |
| Yield Stress at 50 mm/min | 65 | MPa | -- | -- |
| Yield Strain at 50 mm/min | 6 | % | -- | -- |
| Strain at Break at 50 mm/min | 120 | % | -- | -- |
| Flexural Strength at 2 mm/min | 97 | MPa | ASTM D790 | -- |
| Flexural Modulus at 2 mm/min | -- | MPa | -- | -- |
| Izod Notched Impact Strength at 23 °C | 800 | J/m | ASTM D256 | -- |
| Heat Distortion Temp. at 1.82 MPa; 3.2 mm | 130 | °C | ASTM D648 | -- |
| Vicat Softening Temp. at 120 °C/h; 50 N | 150 | °C | ASTM D1525 | -- |
| Haze at 3 mm | < 0.8 | % | ASTM D1003 | -- |
| Light Transmittance at 3 mm | 89 | % | -- | -- |
| Refractive Index | 1.586 | -- | ASTM D542 | -- |
| Flame Rating at 3 mm | HB | -- | UL 94 | -- |
| Flame Rating at 1.5mm | V2 | -- | -- | -- |
| Relative Permittivity at 100 Hz | 3.1 | -- | IEC 60250 | -- |
| Relative Permittivity at 1 MHz | 3 | -- | -- | -- |
| Dissipation Factor at 100 Hz | 5 | 10^-4 | -- | -- |
| Dissipation Factor at 1 MHz | 90 | 10^-4 | -- | -- |
| Volume Resistivity | 10^14 | Ω·m | IEC 60093 | -- |
| Surface resistivity | 10^16 | Ω | -- | -- |
| Electric Strength at 1 mm | 34 | kV/mm | IEC 60243-1 | -- |
| Comparative Tracking Index at Solution A | 250 | V | IEC 60112 | -- |
| Drying Temperature | -- | °C | -- | -- |
| Drying Time | -- | h | -- | -- |
| Injection Temperature | 280 - 310 | °C | -- | -- |
| Mold temperature | 80 | °C | -- | -- |
| Injection Speed | 50 | mm/s | -- | -- |