ACRYPLAS® HD08L
Product Line
| Property Name | Value | Unit |
|---|---|---|
| Appearance | Colourless | -- |
| Physical State | Solid | -- |
| Relative density (water = 1) | 1.19 | -- |
| Decomposition Temperature | >280 | -- |
| Melting point/freezing point | 60-100 | °C |
| Solubility in Water | Immiscible | -- |
| Specification Name | Value | Unit | Test Method | Test Condition |
|---|---|---|---|---|
| Melt flow rate at 230 °C/3.8 Kg | 1.5 | g/10min | ISO 1133 | -- |
| Shrinkage | 0.2 - 0.6 | % | ISO 294 | -- |
| Water absorption at 24hr | 0.3 | % | ISO 62 | -- |
| Density | 1.19 | g/cm3 | ISO 1183 | -- |
| Tensile strength at 5 mm/min | 75 | MPa | ISO 527 | -- |
| Tensile Modulus at 1 mm/min | 3300 | MPa | -- | -- |
| Elongation at 5 mm/min | 6 | % | -- | -- |
| Flexural Strength at 2 mm/min | 130 | MPa | ISO 178 | -- |
| Flexural Modulus at 2 mm/min | 3400 | MPa | -- | -- |
| Charpy impact strength at 1eU unnotched | 20 | KJ/m2 | ISO 179 | -- |
| Charpy impact strength at 1eA notched | 1.6 | KJ/m2 | -- | -- |
| Vicat softening temperature at B50 | 101 | °C | ISO 306 | -- |
| Heat distortion temperature at 1.8MPa | 94 | °C | ISO 75 | -- |
| Thermal expansion coefficient | 6 x 10^-5 | 1/°C | ISO 11359 | -- |
| Transmittance at 3mm | 92 | % | ISO 13468 | -- |
| Haze at 3 mm | < 0.5 | % | ISO 14782 | -- |
| Refractive Index | 1.49 | -- | ISO 489 | -- |
| Flame Rating 1.5 mm/3.0 mm | HB | Class | UL94 | -- |
| Surface resistivity | >10^16 | Ω | ASTM D 527 | -- |
| Volume Resistivity | >10^13 | Ω.m | -- | -- |
| Dielectric strength at 4 kv/sec | -- | kV/mm | ASTM D 149 | -- |
| Dielectric constant at 60 Hz | 3.7 | -- | ASTM D 150 | -- |
| Screw L/D | 25 ~ 35 | -- | -- | -- |
| Barrel temperature (Hopper) | 210 - 240 | °C | -- | -- |
| Barrel temperature (Center) | 220 - 250 | °C | -- | -- |
| Barrel temperature (Die side) | -- | °C | -- | -- |
| Die temperature | -- | °C | -- | -- |