MAGNUM™ 3325 MT | |||
ABS Resin | |||
Overview | Overview: | ||
MAGNUM™ 3325MT is a medium heat ABS. Its inherent low gloss combined with a high flow makes it specifically | |||
suitable for unpainted interior automotive applications. MAGNUM 3325MT can thereby help you to save up to 50% | |||
of the part costs. It is globally available, locally produced in major car production regions. | |||
Benefits: | |||
· Lot to lot consistency allowing for optimal machine parameters settings from the start | |||
· Self-coloring enabling improvement of costs by using less pigments and lowering your logistic costs | |||
· Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints. | |||
· Heat stability during wide range of processing temperatures: enhanced part design freedom | |||
· High scratch and mar resistance for an improved aesthetic durability of the parts | |||
· Easier recyclability of unpainted part | |||
Applications: | |||
· Matt/unpainted interior automotive applications | |||
· Mid-consoles | |||
· Pillars | |||
· Door liners | |||
· Glove boxes | |||
Automotive Specifications | |||
· CHRYSLER MS-DB-191 Type A CPN1497 Color: | · CHRYSLER MS-DB-191 Type A CPN1734 Color: | ||
Black | Color Match | ||
· DAIMLER DBL 5404.80 | · FORD ESB-M4D483-A2 | ||
· FORD WSK-M4D827-A | · FORD WSS-M4D483-C1 | ||
· FORD WSS-M4D827-C1 | · GM GMP.ABS.003 | ||
· GM GMW15572P-ABS-T2 | · RNPO AS31 |
Physical | Nominal Value (SI) | Test Method | |
Density | 1.05 g/cm³ | ISO 1183/B | |
Apparent (Bulk) Density | 0.65 g/cm³ | ISO 60 | |
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 g/10 min | ISO 1133 | |
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 11.0 cm³/10min | ISO 1133 | |
Molding Shrinkage | 0.40 to 0.70 % | ISO 294-4 | |
Mechanical | Nominal Value (SI) | Test Method | |
Tensile Modulus | ISO 527-2 | ||
0.126 in (3.20 mm), Injection Molded | 2200 MPa | ||
Tensile Stress | ISO 527-2/50 | ||
Yield, 0.126 in (3.20 mm), Injection Molded | 43.0 MPa | ||
Tensile Strain | ISO 527-2/50 | ||
Yield, 0.126 in (3.20 mm), Injection Molded | 3.3 % | ||
Flexural Modulus 1, 2 | ISO 178 | ||
0.126 in (3.20 mm), Injection Molded | 2100 MPa | ||
Flexural Stress 1, 2 | ISO 178 | ||
0.126 in (3.20 mm), Injection Molded | 65.0 MPa | ||
Page: 1 of 3 | Form No. 500-00030802en | ||
Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
Charpy Notched Impact Strength | |||
-22°F (-30°C), Compression Molded | 3.8 ft·lb/in² | 8.0 kJ/m² | ISO 179/2 |
-22°F (-30°C), Injection Molded | 5.2 ft·lb/in² | 11 kJ/m² | ISO 179/1eA |
73°F (23°C), Injection Molded | 8.1 ft·lb/in² | 17 kJ/m² | ISO 179/1eA |
73°F (23°C), Compression Molded | 5.7 ft·lb/in² | 12 kJ/m² | ISO 179/2 |
Notched Izod Impact Strength | ISO 180/1A | ||
-22°F (-30°C) | 4.8 ft·lb/in² | 10 kJ/m² | |
73°F (23°C) | 8.1 ft·lb/in² | 17 kJ/m² | |
Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
Heat Deflection Temperature | ISO 75-2/A | ||
264 psi (1.8 MPa), Unannealed | 180 °F | 82.0 °C | |
264 psi (1.8 MPa), Annealed | 214 °F | 101 °C | |
Vicat Softening Temperature | 216 °F | 102 °C | ISO 306/B50 |
Flammability | Nominal Value (English) | Nominal Value (SI) | Test Method |
Burning Rate 3 (0.0787 in (2.00 mm)) | 2.4 in/min | 60 mm/min | ISO 3795 |
Flame Rating 3 | UL 94 | ||
0.06 in (1.5 mm) | HB | HB | |
0.12 in (3.0 mm) | HB | HB | |
Carbon Emission 3 | 20.0 µg/g | 20.0 µg/g | VDA 277 |
Fogging 3 (212°F (100°C)) | 98 % | 98 % | ISO 6452 |