| MAGNUM™ 3416 SC | |
| ABS Resin | |
| Overview | |
| MAGNUM™ 3416SC is the reference high-heat ABS in the automotive industry. It is universally suitable for all | |
| interior and exterior applications. | |
| It is approved at all major OEMs. MAGNUM™ 3416SC is globally available, locally produced in major car production | |
| regions. | |
| Benefits: | |
| · Lot to lot consistency allowing for optimal machine parameters settings from the start | |
| · Self-coloring enabling improvement of costs by using less pigments and lowering your logistic costs | |
| · Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints. | |
| · Heat stability during wide range of processing temperatures: enhanced part design freedom | |
| Applications: | |
| · Main interior and exterior automotive applications | |
| · Mid-consoles | |
| · Door panels | |
| · Door handles | |
| · Pillars | |
| Automotive Specifications | |
| · BMW GS 93016 Color: Natural | · DAIMLER DBL 5404.04 |
| · FORD WSS-M4D690-B1 | · GM GMW15572P-ABS-T2 Color: Natural |
| · JLR STJLR.51.353 | · JLR STJLR.51.5229 |
| · JLR STJLR.51.5262 Color: Natural | · PSA Peugeot-Citroën ABS-0019 |
| · PSA Peugeot-Citroën ABS-0021 | · RNPO AS32-1 |
| · VAG VW-TL 527 A | · VAG VW-TL 527 B |
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method | |
| Density | 1.05 g/cm³ | 1.05 g/cm³ | ISO 1183 | |
| Apparent (Bulk) Density | 0.65 g/cm³ | 0.65 g/cm³ | ISO 60 | |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.5 g/10 min | 6.5 g/10 min | ISO 1133 | |
| Molding Shrinkage | 4.0E-3 to 7.0E-3 in/in | 0.40 to 0.70 % | ISO 294-4 | |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method | |
| Tensile Modulus | 319000 psi | 2200 MPa | ISO 527-2 | |
| Tensile Stress (Yield) | 6240 psi | 43.0 MPa | ISO 527-2 | |
| Tensile Strain (Yield) | 3.1 % | 3.1 % | ISO 527-2 | |
| Flexural Modulus 1 | 319000 psi | 2200 MPa | ISO 178 | |
| Flexural Stress 1 | 11000 psi | 76.0 MPa | ISO 178 | |
| Impact | Nominal Value (English) | Nominal Value (SI) | Test Method | |
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -22°F (-30°C) | 5.7 ft·lb/in² | 12 kJ/m² | ||
| 73°F (23°C) | 8.1 ft·lb/in² | 17 kJ/m² | ||
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method | |
| Heat Deflection Temperature | ISO 75-2/A | |||
| 264 psi (1.8 MPa), Unannealed | 185 °F | 85.0 °C | ||
| 264 psi (1.8 MPa), Annealed | 212 °F | 100 °C | ||
| Vicat Softening Temperature | 226 °F | 108 °C | ISO 306/B50 | |
| Page: 1 of 3 | Form No. 500-00031908en | |||
| Flammability | Nominal Value (English) | Nominal Value (SI) | Test Method | |
| Burning Rate 2 (0.0787 in (2.00 mm)) | 2.2 in/min | 55 mm/min | ISO 3795 | |
| Flame Rating 2 | UL 94 | |||
| 0.06 in (1.5 mm) | HB | HB | ||
| 0.12 in (3.0 mm) | HB | HB | ||
| Carbon Emission | 10.0 µg/g | 10.0 µg/g | VDA 277 | |
| Fogging | 99 % | 99 % | ISO 6452 |