WANSUPER® 5017 POLYOLEFIN ELASTOMER (POE)
| Property Name | Value | Unit |
|---|---|---|
| Appearance | Colourless | -- |
| Physical State | Solid | -- |
| Relative density (water = 1) | 0.84-0.94 | -- |
| Molecular Weight | >10000 | g/mol |
| Solubility in Water | Immiscible | -- |
| Specification Name | Value | Unit | Test Method | Test Condition |
|---|---|---|---|---|
| Melt index at 2.16 kg/190 °C) | 1 | g/10 min | ASTM D1238 | -- |
| Density | 0.87 | g/cm3 | ASTM D792 | -- |
| Mooney viscosity at ML 1+4, 121°C | 23 | MU | ASTM D1646 | -- |
| Tensile modulus at 100% secant, 500 mm/min | 2.9 | MPa | ASTM D638 | -- |
| Tensile strength at break at 500 mm/min | 9.5 | MPa | -- | -- |
| Elongation at break at 500 mm/min | 800 | % | -- | -- |
| Flexural modulus at 1% secant | 13.7 | MPa | ASTM D790 | -- |
| Tear strength (Type C) | 40 | kN/m | ASTM D624 | -- |
| Hardness at Shore A, 1 sec | 73 | -- | ASTM D2240 | -- |
| Hardness at Shore D,1 sec | 22 | -- | -- | -- |
| Melting temperature | 62 | °C | Wanhua method | -- |
| DSC Glass transition temperature | -52 | °C | -- | -- |